Search Results
Search Filters
-
Ductile Iron Bar x
Filter Your Search
Shop by Category
- Accessories(549)
- Braided Packing(124)
- Acrylic Graphite Packing ML402(8)
- Acrylic PTFE Packing ML2225(8)
- Aramid PTFE Packing ML4800(8)
- Carbon PTFE Packing ML4461(8)
- Flax PTFE Packing 219(8)
- Flexible Graphite Packing ML2001(10)
- GFO® Packing ML4002(8)
- High Performance Carbon Packing ML560(8)
- High Performance PTFE Packing ML2240(8)
- Pre-lubricated PTFE Packing ML2235(8)
- PTFE Packing ML2238(8)
- PTFE Graphite Packing ML3600(8)
- Tek-Pro Aramid PTFE Packing ML6225(8)
- Lantern Rings(8)
- Seating Tools(6)
- Packing Hooks(3)
- Packing Lube(1)
- Cylinder Components(768)
- Cylinder Repair Bench Products(19)
- Kraken Bearings(48)
- Round Bar(245)
- Seals(26,284)
- Seal Kits(17,589)
- Tube(328)
DUCT-4000 has a diameter of 4 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-3500 has a diameter of 3.5 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-2500 has a diameter of 2.5 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-10000 has a diameter of 10 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-2000 has a diameter of 2 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-5000 has a diameter of 5 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-3000 has a diameter of 3 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-6000 has a diameter of 6 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-4500 has a diameter of 4.5 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
DUCT-7000 has a diameter of 7 in. The material is 65-45-12 Ductile Iron.
65-45-12 Ductile Iron is used to machine pistons, glands, caps, manifolds, rams, and valve bodies.
Ductile has higher machining speeds than steel and there is usually no need for deburring machined parts. The graphite flakes in the material act as a self-lubricant. Ductile can be flame or induction hardened as well as deep hardened.
Ductile bars are produced with sufficient stock on the outside diameter to ensure clean-up at the nominal dimension.
- Excellent machinability
- Optimal impact strengths
- Optimal fatigue properties
- Optimal electrical conductivity
- High magnetic permeability
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.