8 in Induction Hardened Chrome Shafting
View Related Items
92A Durometer | Urethane Material | 8 in Nominal Inner Diameter
This tube has been produced using the cold drawing process and is seamless. The cold drawing process produces higher physical properties without additional heat treating resulting in good strength to weight ratios.
14.000 × 16.000 Honed Tube HF A106 B/C
IHCP-8000 Induction Hardened Chrome Shafting
8 in induction hardened chrome shafting.
The base material is 1045/1050 Carbon Steel with 0.0005 in (0.0127mm minimum)-thick chrome plating and a case depth of 0.05 in (1.27 mm).
Induction Hardened Chrome is typically used in abrasive envrionments where the cylinder is exposed to rocks or heavy debris. Also used to machine clevis pins.
- Greater strength
- Better resistance to mechanical damage
Full mill lengths will be cut to lengths between 12 ft and 19 ft long. Packages longer than 44 inches may have additional freight charges.
Export To PDF
Item Specifications
-
0.05 in (1.27 mm)
-
Induction Hardened Chrome
-
0.0005 in (0.0127mm minimum)
-
10%
-
Rc 68-72
-
1045/1050 Carbon Steel
-
ASTM A311, Class B
-
8 in
-
372 in
-
0.006 in TIR per ft
-
Ra 12 max
-
115,000 psi
-
inch
-
50,000 psi
-
14.26 lbs per IN
View Related Items
92A Durometer | Urethane Material | 8 in Nominal Inner Diameter
This tube has been produced using the cold drawing process and is seamless. The cold drawing process produces higher physical properties without additional heat treating resulting in good strength to weight ratios.
14.000 × 16.000 Honed Tube HF A106 B/C